# Data set for Damage Model v.1.0
#
model_tag= DMG

# Fields in the data set
# material - Tag for material
# G - Shear modulus
# Bulk - Bulk modulus
# a - Constant to adjust shear modulus due to variation of temperature from initial
# b - Constant to adjust bulk modulus due to variation of temperature from initial
# Tmelt - Melt temperature (K)
# heat - Heat generation term
# Kic - Particle fracture toughness
# nv - Particle McClintock damage constant
# fname - Tag for data set
# source - Source of data set
# comment - Any other comment on data set
# excluded - Is dataset excluded? 0=no, 1=yes
# dstype - Experiment type: 1=Tension 2=Compression 3=Torsion 4=Tens+Comp 5=Comp+Tens
# units - Stress units: 1=psi 2=Ksi 3=Pa  4=KPa 5=MPa 6=GPa
# Tinit - Initial temperature
# strain - strain values
# stress - stress values
# dn - Particle average size
# fn - Particles volume fraction
# dcs0 - Reference grain size or dendrite cell size
# dcs - Grain size or dendrite cell size of experiment sample
# r0 - Initial radius of a spherical void
# volF - Initial void volume fraction
# period - Time period (0=no model)
# rate - Strain rate
# incr - No. of increments (0=no model)
# angle - Bi-axial loading ratio
# e_load - Strain level for load change (dstype 4 & 5)
#
material= ti06al04v
G= 0
Bulk= 0
a= 0
b= 0
Tmelt= 3000
heat= 0.34
Kic= 1000
nv= 0.3
fname= C1R4N3.B1
source= DR. T. NICHOLAS; MATERIAL BEHAVIOR AT HIGH STRAIN RATES; WRIGHT-PATTERSON AFB, OHIO
comment= TRUE STRESS V. TRUE STRAIN; SOURCE: MAIDEN AND GREEN; FIG. 34
excluded= 0
dstype= 2
units= 5
Tinit= 293
dn= 0
fn= 0.001
dcs0= 30
dcs= 30
r0= 0
volF= 0
period= 20
rate= 0.004
incr= 100
angle= 0.51
e_load= 0
btype= 0

# Experimental data
strain, stress=
0.02 1201.3
0.04 1252
0.06 1280.8
0.08 1295