# Data set for Damage Model v.1.0
#
model_tag= DMG

# Fields in the data set
# material - Tag for material
# G - Shear modulus
# Bulk - Bulk modulus
# a - Constant to adjust shear modulus due to variation of temperature from initial
# b - Constant to adjust bulk modulus due to variation of temperature from initial
# Tmelt - Melt temperature (K)
# heat - Heat generation term
# Kic - Particle fracture toughness
# nv - Particle McClintock damage constant
# fname - Tag for data set
# source - Source of data set
# comment - Any other comment on data set
# excluded - Is dataset excluded? 0=no, 1=yes
# dstype - Experiment type: 1=Tension 2=Compression 3=Torsion 4=Tens+Comp 5=Comp+Tens
# units - Stress units: 1=psi 2=Ksi 3=Pa  4=KPa 5=MPa 6=GPa
# Tinit - Initial temperature
# strain - strain values
# stress - stress values
# dn - Particle average size
# fn - Particles volume fraction
# dcs0 - Reference grain size or dendrite cell size
# dcs - Grain size or dendrite cell size of experiment sample
# r0 - Initial radius of a spherical void
# volF - Initial void volume fraction
# period - Time period (0=no model)
# rate - Strain rate
# incr - No. of increments (0=no model)
# angle - Bi-axial loading ratio
# e_load - Strain level for load change (dstype 4 & 5)
#
material= hy100steel
G= 0
Bulk= 0
a= 0
b= 0
Tmelt= 3000
heat= 0.34
Kic= 1000
nv= 0.3
fname= T4R6P2.A1
source= HONEYWELL; G.R. JOHNSON AND T.J. HOLMQUIST; TEST DATA AND COMPUTATIONAL STRENGTH AND FRACTURE MODEL CONSTANTS FOR 23 MATERIALS SUBJECTED TO LARGE STRAINS, HIGH STRAIN RATES, AND HIGH TEMPERATURES; SEPTEMBER 1988
comment= TRUE STRESS V. TRUE STRAIN
excluded= 0
dstype= 1
units= 5
Tinit= 822
dn= 0
fn= 0.001
dcs0= 30
dcs= 30
r0= 0
volF= 0
period= 0.000252576
rate= 594
incr= 100
angle= 0.51
e_load= 0
btype= 0

# Experimental data
strain, stress=
-6.333e-005 0.43334
0.00010468 86.963
-4.141e-005 169.14
-0.00018992 261.32
-0.00021321 356.98
-0.00017232 447.86
-0.00019436 538.3
-0.00014594 598.3
-0.00021702 631.35
0.0060803 652.73
0.01345 671.94
0.020694 686.82
0.027371 701.26
0.034995 710.43
0.042367 718.77
0.050747 725.87
0.059318 729.87
0.067826 732.15
0.076334 732.22
0.086419 728.42
0.096 722.01
0.10401 715.6
0.11308 708.29
0.12096 701.05
0.1296 688.08
0.139 672.1
0.14562 658.69
0.15003 646.57