# Data set for Damage Model v.1.0
#
model_tag= DMG

# Fields in the data set
# material - Tag for material
# G - Shear modulus
# Bulk - Bulk modulus
# a - Constant to adjust shear modulus due to variation of temperature from initial
# b - Constant to adjust bulk modulus due to variation of temperature from initial
# Tmelt - Melt temperature (K)
# heat - Heat generation term
# Kic - Particle fracture toughness
# nv - Particle McClintock damage constant
# fname - Tag for data set
# source - Source of data set
# comment - Any other comment on data set
# excluded - Is dataset excluded? 0=no, 1=yes
# dstype - Experiment type: 1=Tension 2=Compression 3=Torsion 4=Tens+Comp 5=Comp+Tens
# units - Stress units: 1=psi 2=Ksi 3=Pa  4=KPa 5=MPa 6=GPa
# Tinit - Initial temperature
# strain - strain values
# stress - stress values
# dn - Particle average size
# fn - Particles volume fraction
# dcs0 - Reference grain size or dendrite cell size
# dcs - Grain size or dendrite cell size of experiment sample
# r0 - Initial radius of a spherical void
# volF - Initial void volume fraction
# period - Time period (0=no model)
# rate - Strain rate
# incr - No. of increments (0=no model)
# angle - Bi-axial loading ratio
# e_load - Strain level for load change (dstype 4 & 5)
#
material= hy100steel
G= 0
Bulk= 0
a= 0
b= 0
Tmelt= 3000
heat= 0.34
Kic= 1000
nv= 0.3
fname= T3R6P2.A1
source= HONEYWELL; G.R. JOHNSON AND T.J. HOLMQUIST; TEST DATA AND COMPUTATIONAL STRENGTH AND FRACTURE MODEL CONSTANTS FOR 23 MATERIALS SUBJECTED TO LARGE STRAINS, HIGH STRAIN RATES, AND HIGH TEMPERATURES; SEPTEMBER 1988
comment= TRUE STRESS V. TRUE STRAIN
excluded= 0
dstype= 1
units= 5
Tinit= 672
dn= 0
fn= 0.001
dcs0= 30
dcs= 30
r0= 0
volF= 0
period= 0.000260225
rate= 578
incr= 100
angle= 0.51
e_load= 0
btype= 0

# Experimental data
strain, stress=
1.3411e-007 -0.0018937
-0.00015055 80.889
-0.00011665 176.57
-0.00020722 267.03
-0.00029777 357.49
-0.00032173 436.21
-0.00034651 517.54
-0.00037126 598.86
-0.00045229 658.01
-0.00045864 678.89
0.0059639 698.57
0.011631 715.19
0.017614 730.91
0.023471 743.18
0.031345 758.9
0.039093 771.24
0.048922 780.48
0.058625 789.79
0.068833 796.48
0.080178 797.51
0.091837 796.75
0.10362 794.34
0.1139 785.79
0.12348 773.72
0.13395 755.66
0.14335 737.04
0.15041 718.91