# Data set for Damage Model v.1.0
#
model_tag= DMG

# Fields in the data set
# material - Tag for material
# G - Shear modulus
# Bulk - Bulk modulus
# a - Constant to adjust shear modulus due to variation of temperature from initial
# b - Constant to adjust bulk modulus due to variation of temperature from initial
# Tmelt - Melt temperature (K)
# heat - Heat generation term
# Kic - Particle fracture toughness
# nv - Particle McClintock damage constant
# fname - Tag for data set
# source - Source of data set
# comment - Any other comment on data set
# excluded - Is dataset excluded? 0=no, 1=yes
# dstype - Experiment type: 1=Tension 2=Compression 3=Torsion 4=Tens+Comp 5=Comp+Tens
# units - Stress units: 1=psi 2=Ksi 3=Pa  4=KPa 5=MPa 6=GPa
# Tinit - Initial temperature
# strain - strain values
# stress - stress values
# dn - Particle average size
# fn - Particles volume fraction
# dcs0 - Reference grain size or dendrite cell size
# dcs - Grain size or dendrite cell size of experiment sample
# r0 - Initial radius of a spherical void
# volF - Initial void volume fraction
# period - Time period (0=no model)
# rate - Strain rate
# incr - No. of increments (0=no model)
# angle - Bi-axial loading ratio
# e_load - Strain level for load change (dstype 4 & 5)
#
material= hy100steel
G= 0
Bulk= 0
a= 0
b= 0
Tmelt= 3000
heat= 0.34
Kic= 1000
nv= 0.3
fname= T1R9P2.B1
source= DR. T. NICHOLAS; MATERIAL BEHAVIOR AT HIGH STRAIN RATES; WRIGHT-PATTERSON AFB, OHIO
comment= STRESS V. STRAIN; REF: BLESS, UDRI (1984)
excluded= 0
dstype= 1
units= 5
Tinit= 293
dn= 0
fn= 0.001
dcs0= 30
dcs= 30
r0= 0
volF= 0
period= 0.000311726
rate= 950
incr= 100
angle= 0.51
e_load= 0
btype= 0

# Experimental data
strain, stress=
1.1474e-006 0.25806
0.00015505 80.424
0.0010066 150.97
0.0013981 245.35
0.0018216 325.78
0.0022702 424.73
0.002678 512.01
0.0031336 607.91
0.0036095 694.94
0.0042304 777.65
0.0047739 864.68
0.0055736 928.38
0.022286 946.42
0.035902 959.8
0.051026 963.59
0.067489 972.49
0.086402 973.61
0.1014 973.59
0.11167 971.13
0.12492 970.54
0.13871 964.9
0.15427 955.51
0.16489 949.26
0.17817 930.92
0.19235 905.76
0.20572 878.28
0.21896 850.3
0.23588 806.45
0.24962 765.8
0.26214 728.16
0.27318 687.42
0.28394 649.21
0.29285 621.34
0.29614 601.66