# Data set for Damage Model v.1.0
#
model_tag= DMG

# Fields in the data set
# material - Tag for material
# G - Shear modulus
# Bulk - Bulk modulus
# a - Constant to adjust shear modulus due to variation of temperature from initial
# b - Constant to adjust bulk modulus due to variation of temperature from initial
# Tmelt - Melt temperature (K)
# heat - Heat generation term
# Kic - Particle fracture toughness
# nv - Particle McClintock damage constant
# fname - Tag for data set
# source - Source of data set
# comment - Any other comment on data set
# excluded - Is dataset excluded? 0=no, 1=yes
# dstype - Experiment type: 1=Tension 2=Compression 3=Torsion 4=Tens+Comp 5=Comp+Tens
# units - Stress units: 1=psi 2=Ksi 3=Pa  4=KPa 5=MPa 6=GPa
# Tinit - Initial temperature
# strain - strain values
# stress - stress values
# dn - Particle average size
# fn - Particles volume fraction
# dcs0 - Reference grain size or dendrite cell size
# dcs - Grain size or dendrite cell size of experiment sample
# r0 - Initial radius of a spherical void
# volF - Initial void volume fraction
# period - Time period (0=no model)
# rate - Strain rate
# incr - No. of increments (0=no model)
# angle - Bi-axial loading ratio
# e_load - Strain level for load change (dstype 4 & 5)
#
material= 321ss
G= 0
Bulk= 0
a= 0
b= 0
Tmelt= 3000
heat= 0.34
Kic= 1000
nv= 0.3
fname= T1R9P2.A1
source= DR. T. NICHOLAS; MATERIAL BEHAVIOR AT HIGH STRAIN RATES; WRIGHT-PATTERSON AFB, OHIO
comment= STRESS V. STRAIN; FIG. 11
excluded= 0
dstype= 1
units= 5
Tinit= 293
dn= 0
fn= 0.001
dcs0= 30
dcs= 30
r0= 0
volF= 0
period= 0.000261211
rate= 900
incr= 100
angle= 0.51
e_load= 0
btype= 0

# Experimental data
strain, stress=
0.0026827 0.72401
0.0028347 63.357
0.0028726 145.33
0.0028265 230.7
0.0025272 326.45
0.0028371 404.86
0.0034552 483.79
0.0045129 542.63
0.0065306 587.71
0.0089829 623.27
0.011375 648.78
0.014289 670.56
0.019502 693.33
0.026521 716.15
0.035781 739.39
0.04834 763.17
0.064858 791.37
0.083626 818.4
0.097399 837.43
0.11167 856.67
0.12724 877.56
0.1433 898.24
0.1582 916.31
0.17725 938.58
0.19383 956.71
0.21097 976.43
0.22489 991.6
0.23509 1003.9