# Data set for Damage Model v.1.0
#
model_tag= DMG

# Fields in the data set
# material - Tag for material
# G - Shear modulus
# Bulk - Bulk modulus
# a - Constant to adjust shear modulus due to variation of temperature from initial
# b - Constant to adjust bulk modulus due to variation of temperature from initial
# Tmelt - Melt temperature (K)
# heat - Heat generation term
# Kic - Particle fracture toughness
# nv - Particle McClintock damage constant
# fname - Tag for data set
# source - Source of data set
# comment - Any other comment on data set
# excluded - Is dataset excluded? 0=no, 1=yes
# dstype - Experiment type: 1=Tension 2=Compression 3=Torsion 4=Tens+Comp 5=Comp+Tens
# units - Stress units: 1=psi 2=Ksi 3=Pa  4=KPa 5=MPa 6=GPa
# Tinit - Initial temperature
# strain - strain values
# stress - stress values
# dn - Particle average size
# fn - Particles volume fraction
# dcs0 - Reference grain size or dendrite cell size
# dcs - Grain size or dendrite cell size of experiment sample
# r0 - Initial radius of a spherical void
# volF - Initial void volume fraction
# period - Time period (0=no model)
# rate - Strain rate
# incr - No. of increments (0=no model)
# angle - Bi-axial loading ratio
# e_load - Strain level for load change (dstype 4 & 5)
#
material= 304ss
G= 0
Bulk= 0
a= 0
b= 0
Tmelt= 3000
heat= 0.34
Kic= 1000
nv= 0.3
fname= T1R9P2.A1
source= DR. T. NICHOLAS; MATERIAL BEHAVIOR AT HIGH STRAIN RATES; WRIGHT-PATTERSON AFB, OHIO
comment= STRESS V. STRAIN; FIG. 10
excluded= 0
dstype= 1
units= 5
Tinit= 293
dn= 0
fn= 0.001
dcs0= 30
dcs= 30
r0= 0
volF= 0
period= 0.0002435
rate= 900
incr= 100
angle= 0.51
e_load= 0
btype= 0

# Experimental data
strain, stress=
6.5956e-005 0.0022093
9.7942e-005 63.051
6.1874e-005 139.3
0.00014427 212.92
2.8763e-005 286.01
0.000364 369.49
0.00051426 449.1
0.00063059 522.01
0.0023805 607.84
0.0035135 644.33
0.0048844 671.67
0.0059601 692.5
0.0082635 715.46
0.01155 737.04
0.015172 756.76
0.02017 774.69
0.026282 791.1
0.034609 807.58
0.046874 831.98
0.062774 858.94
0.077976 881.97
0.092727 903.96
0.10917 927.27
0.12425 947.33
0.14361 972.98
0.16174 996.15
0.1793 1018.1
0.19912 1042.7
0.21915 1064.5