# Data set for Damage Model v.1.0
#
model_tag= DMG

# Fields in the data set
# material - Tag for material
# G - Shear modulus
# Bulk - Bulk modulus
# a - Constant to adjust shear modulus due to variation of temperature from initial
# b - Constant to adjust bulk modulus due to variation of temperature from initial
# Tmelt - Melt temperature (K)
# heat - Heat generation term
# Kic - Particle fracture toughness
# nv - Particle McClintock damage constant
# fname - Tag for data set
# source - Source of data set
# comment - Any other comment on data set
# excluded - Is dataset excluded? 0=no, 1=yes
# dstype - Experiment type: 1=Tension 2=Compression 3=Torsion 4=Tens+Comp 5=Comp+Tens
# units - Stress units: 1=psi 2=Ksi 3=Pa  4=KPa 5=MPa 6=GPa
# Tinit - Initial temperature
# strain - strain values
# stress - stress values
# dn - Particle average size
# fn - Particles volume fraction
# dcs0 - Reference grain size or dendrite cell size
# dcs - Grain size or dendrite cell size of experiment sample
# r0 - Initial radius of a spherical void
# volF - Initial void volume fraction
# period - Time period (0=no model)
# rate - Strain rate
# incr - No. of increments (0=no model)
# angle - Bi-axial loading ratio
# e_load - Strain level for load change (dstype 4 & 5)
#
material= 1020steel
G= 0
Bulk= 0
a= 0
b= 0
Tmelt= 3000
heat= 0.34
Kic= 1000
nv= 0.3
fname= T1R8P2.A1
source= DR. T. NICHOLAS; MATERIAL BEHAVIOR AT HIGH STRAIN RATES; WRIGHT-PATTERSON AFB, OHIO
comment= STRESS V. STRAIN; FIG. 8
excluded= 0
dstype= 1
units= 5
Tinit= 293
dn= 0
fn= 0.001
dcs0= 30
dcs= 30
r0= 0
volF= 0
period= 0.000247325
rate= 800
incr= 100
angle= 0.51
e_load= 0
btype= 0

# Experimental data
strain, stress=
9.1448e-005 0.51377
3.5887e-005 51.153
0.00013785 106.38
0.0002449 144.31
0.00037029 195.31
0.00050444 244.71
0.00069144 309.12
0.00063859 375.97
0.00076904 450.6
0.0010869 515.9
0.0015449 572.2
0.0021149 624.65
0.0027183 679.21
0.0035377 743.87
0.0045637 811.99
0.0051534 844.53
0.0054593 846.46
0.0060416 847.63
0.0065017 846.26
0.0068321 843.77
0.007138 804.82
0.007518 752.49
0.0079293 694.43
0.0082409 670.85
0.0088757 662.44
0.0099917 657.06
0.012007 652.65
0.014822 651.12
0.024347 655.62
0.037845 661.7
0.051033 666.68
0.06567 671.62
0.080268 675.32
0.096404 679.14
0.11494 683.52
0.13256 687.47
0.1497 691.06
0.16571 693.4
0.18258 695.4
0.19786 697.74