# Data set for Damage Model v.1.0
#
model_tag= DMG

# Fields in the data set
# material - Tag for material
# G - Shear modulus
# Bulk - Bulk modulus
# a - Constant to adjust shear modulus due to variation of temperature from initial
# b - Constant to adjust bulk modulus due to variation of temperature from initial
# Tmelt - Melt temperature (K)
# heat - Heat generation term
# Kic - Particle fracture toughness
# nv - Particle McClintock damage constant
# fname - Tag for data set
# source - Source of data set
# comment - Any other comment on data set
# excluded - Is dataset excluded? 0=no, 1=yes
# dstype - Experiment type: 1=Tension 2=Compression 3=Torsion 4=Tens+Comp 5=Comp+Tens
# units - Stress units: 1=psi 2=Ksi 3=Pa  4=KPa 5=MPa 6=GPa
# Tinit - Initial temperature
# strain - strain values
# stress - stress values
# dn - Particle average size
# fn - Particles volume fraction
# dcs0 - Reference grain size or dendrite cell size
# dcs - Grain size or dendrite cell size of experiment sample
# r0 - Initial radius of a spherical void
# volF - Initial void volume fraction
# period - Time period (0=no model)
# rate - Strain rate
# incr - No. of increments (0=no model)
# angle - Bi-axial loading ratio
# e_load - Strain level for load change (dstype 4 & 5)
#
material= 304ss
G= 0
Bulk= 0
a= 0
b= 0
Tmelt= 3000
heat= 0.34
Kic= 1000
nv= 0.3
fname= T1R4P0.A1
source= DR. T. NICHOLAS; MATERIAL BEHAVIOR AT HIGH STRAIN RATES; WRIGHT-PATTERSON AFB, OHIO
comment= STRESS V. STRAIN; FIG. 10
excluded= 0
dstype= 1
units= 5
Tinit= 293
dn= 0
fn= 0.001
dcs0= 30
dcs= 30
r0= 0
volF= 0
period= 0.0572625
rate= 4
incr= 100
angle= 0.51
e_load= 0
btype= 0

# Experimental data
strain, stress=
6.5136e-005 0.1783
2.4624e-005 75.373
8.8959e-005 145.11
6.7329e-005 224.36
0.00015465 302.57
0.00035334 371.78
0.0007863 446.65
0.00075577 481.16
0.0015033 502.49
0.0032352 522.28
0.0065586 550.04
0.011259 575.91
0.017656 601.14
0.024088 618.97
0.031502 635.6
0.045787 659.68
0.062219 684.55
0.080213 709.46
0.095365 729.32
0.11298 752.35
0.13358 777.17
0.15191 799.23
0.1731 823.43
0.19235 845.57
0.20972 863.77
0.22905 882.18