# Data set for Damage Model v.1.0
#
model_tag= DMG

# Fields in the data set
# material - Tag for material
# G - Shear modulus
# Bulk - Bulk modulus
# a - Constant to adjust shear modulus due to variation of temperature from initial
# b - Constant to adjust bulk modulus due to variation of temperature from initial
# Tmelt - Melt temperature (K)
# heat - Heat generation term
# Kic - Particle fracture toughness
# nv - Particle McClintock damage constant
# fname - Tag for data set
# source - Source of data set
# comment - Any other comment on data set
# excluded - Is dataset excluded? 0=no, 1=yes
# dstype - Experiment type: 1=Tension 2=Compression 3=Torsion 4=Tens+Comp 5=Comp+Tens
# units - Stress units: 1=psi 2=Ksi 3=Pa  4=KPa 5=MPa 6=GPa
# Tinit - Initial temperature
# strain - strain values
# stress - stress values
# dn - Particle average size
# fn - Particles volume fraction
# dcs0 - Reference grain size or dendrite cell size
# dcs - Grain size or dendrite cell size of experiment sample
# r0 - Initial radius of a spherical void
# volF - Initial void volume fraction
# period - Time period (0=no model)
# rate - Strain rate
# incr - No. of increments (0=no model)
# angle - Bi-axial loading ratio
# e_load - Strain level for load change (dstype 4 & 5)
#
material= 10b22steel
G= 0
Bulk= 0
a= 0
b= 0
Tmelt= 3000
heat= 0.34
Kic= 1000
nv= 0.3
fname= T1R4P0.A1
source= DR. T. NICHOLAS; MATERIAL BEHAVIOR AT HIGH STRAIN RATES; WRIGHT-PATTERSON AFB, OHIO
comment= STRESS V. STRAIN; FIG. 16
excluded= 0
dstype= 1
units= 5
Tinit= 293
dn= 0
fn= 0.001
dcs0= 30
dcs= 30
r0= 0
volF= 0
period= 0.0210228
rate= 4
incr= 100
angle= 0.51
e_load= 0
btype= 0

# Experimental data
strain, stress=
0.0018155 0.26285
0.0019762 80.399
0.0021592 168.29
0.002477 261.64
0.0027287 345.13
0.0030458 438.66
0.003439 539.41
0.0039151 632.06
0.004311 718.57
0.0046523 805.71
0.0050771 884.66
0.005334 939.61
0.0057941 941.4
0.0059976 956.02
0.0066491 962.02
0.0080268 968.08
0.008152 962.43
0.0079203 955.26
0.0082483 950.85
0.0088344 946.85
0.010135 946.02
0.012145 949.26
0.017818 958.16
0.028032 973.53
0.038972 988.84
0.04873 1001.2
0.054623 1007
0.058716 1008.3
0.06292 1007.9
0.068704 1001.4
0.075535 992.22
0.084091 979.87