# Data set for Damage Model v.1.0
#
model_tag= DMG

# Fields in the data set
# material - Tag for material
# G - Shear modulus
# Bulk - Bulk modulus
# a - Constant to adjust shear modulus due to variation of temperature from initial
# b - Constant to adjust bulk modulus due to variation of temperature from initial
# Tmelt - Melt temperature (K)
# heat - Heat generation term
# Kic - Particle fracture toughness
# nv - Particle McClintock damage constant
# fname - Tag for data set
# source - Source of data set
# comment - Any other comment on data set
# excluded - Is dataset excluded? 0=no, 1=yes
# dstype - Experiment type: 1=Tension 2=Compression 3=Torsion 4=Tens+Comp 5=Comp+Tens
# units - Stress units: 1=psi 2=Ksi 3=Pa  4=KPa 5=MPa 6=GPa
# Tinit - Initial temperature
# strain - strain values
# stress - stress values
# dn - Particle average size
# fn - Particles volume fraction
# dcs0 - Reference grain size or dendrite cell size
# dcs - Grain size or dendrite cell size of experiment sample
# r0 - Initial radius of a spherical void
# volF - Initial void volume fraction
# period - Time period (0=no model)
# rate - Strain rate
# incr - No. of increments (0=no model)
# angle - Bi-axial loading ratio
# e_load - Strain level for load change (dstype 4 & 5)
#
material= 10b22steel
G= 0
Bulk= 0
a= 0
b= 0
Tmelt= 3000
heat= 0.34
Kic= 1000
nv= 0.3
fname= T1R4N4.A1
source= DR. T. NICHOLAS; MATERIAL BEHAVIOR AT HIGH STRAIN RATES; WRIGHT-PATTERSON AFB, OHIO
comment= STRESS V. STRAIN; FIG. 16
excluded= 0
dstype= 1
units= 5
Tinit= 293
dn= 0
fn= 0.001
dcs0= 30
dcs= 30
r0= 0
volF= 0
period= 281.775
rate= 0.0004
incr= 100
angle= 0.51
e_load= 0
btype= 0

# Experimental data
strain, stress=
0.0018641 0.61135
0.002099 76.186
0.0023082 158.63
0.0024386 248.29
0.0028319 336.9
0.003028 422.87
0.0033718 497.04
0.0037853 594.11
0.004281 683.09
0.0046625 774.9
0.0049635 860.46
0.0051344 897.83
0.0058407 903
0.0070311 903.34
0.007209 897.41
0.0075876 893.21
0.0088863 892.38
0.011409 896.86
0.020051 913.96
0.028541 930.37
0.037709 945.4
0.042291 953.67
0.046224 955.12
0.050422 954.92
0.056761 950.78
0.065293 942.02
0.077582 926.3
0.087792 912.51
0.096861 898.66
0.10609 884.59
0.11271 874.32