# Data set for Damage Model v.1.0
#
model_tag= DMG

# Fields in the data set
# material - Tag for material
# G - Shear modulus
# Bulk - Bulk modulus
# a - Constant to adjust shear modulus due to variation of temperature from initial
# b - Constant to adjust bulk modulus due to variation of temperature from initial
# Tmelt - Melt temperature (K)
# heat - Heat generation term
# Kic - Particle fracture toughness
# nv - Particle McClintock damage constant
# fname - Tag for data set
# source - Source of data set
# comment - Any other comment on data set
# excluded - Is dataset excluded? 0=no, 1=yes
# dstype - Experiment type: 1=Tension 2=Compression 3=Torsion 4=Tens+Comp 5=Comp+Tens
# units - Stress units: 1=psi 2=Ksi 3=Pa  4=KPa 5=MPa 6=GPa
# Tinit - Initial temperature
# strain - strain values
# stress - stress values
# dn - Particle average size
# fn - Particles volume fraction
# dcs0 - Reference grain size or dendrite cell size
# dcs - Grain size or dendrite cell size of experiment sample
# r0 - Initial radius of a spherical void
# volF - Initial void volume fraction
# period - Time period (0=no model)
# rate - Strain rate
# incr - No. of increments (0=no model)
# angle - Bi-axial loading ratio
# e_load - Strain level for load change (dstype 4 & 5)
#
material= c1008steel
G= 0
Bulk= 0
a= 0
b= 0
Tmelt= 3000
heat= 0.34
Kic= 1000
nv= 0.3
fname= T1R2P3.A1
source= DR. T. NICHOLAS; MATERIAL BEHAVIOR AT HIGH STRAIN RATES; WRIGHT-PATTERSON AFB, OHIO
comment= STRESS V. STRAIN; REF: BLESS, UDRI (1984)
excluded= 0
dstype= 1
units= 5
Tinit= 293
dn= 0
fn= 0.001
dcs0= 30
dcs= 30
r0= 0
volF= 0
period= 0.000279331
rate= 1750
incr= 100
angle= 0.51
e_load= 0
btype= 0

# Experimental data
strain, stress=
8.5622e-005 0.12851
0.00029147 39.794
0.00020882 83.637
0.00044291 133.03
0.00027511 184.08
8.1554e-005 240.18
0.0012619 313.17
0.0018506 371.4
0.0024788 433.04
0.0027235 468.79
0.0030218 501.88
0.0031488 512.87
0.0032184 533.46
0.0035444 568.95
0.0039147 615.56
0.0043044 649.29
0.0043788 655.73
0.0058564 659.73
0.0083292 662.45
0.014067 663.56
0.023168 664.34
0.03953 666.82
0.054543 669.2
0.075869 671.43
0.1029 671.74
0.13068 672.15
0.15796 671.69
0.16847 671.04
0.1915 667.41
0.21587 663.74
0.23594 659.68
0.26305 652.41
0.28343 645.31
0.30515 638.05
0.32557 627.03
0.34286 615.71
0.36184 604.1
0.38268 586
0.40532 563.55
0.42324 541.23
0.44567 507.67
0.46012 483.16
0.47489 456.88
0.48883 432