# Data set for Damage Model v.1.0
#
model_tag= DMG

# Fields in the data set
# material - Tag for material
# G - Shear modulus
# Bulk - Bulk modulus
# a - Constant to adjust shear modulus due to variation of temperature from initial
# b - Constant to adjust bulk modulus due to variation of temperature from initial
# Tmelt - Melt temperature (K)
# heat - Heat generation term
# Kic - Particle fracture toughness
# nv - Particle McClintock damage constant
# fname - Tag for data set
# source - Source of data set
# comment - Any other comment on data set
# excluded - Is dataset excluded? 0=no, 1=yes
# dstype - Experiment type: 1=Tension 2=Compression 3=Torsion 4=Tens+Comp 5=Comp+Tens
# units - Stress units: 1=psi 2=Ksi 3=Pa  4=KPa 5=MPa 6=GPa
# Tinit - Initial temperature
# strain - strain values
# stress - stress values
# dn - Particle average size
# fn - Particles volume fraction
# dcs0 - Reference grain size or dendrite cell size
# dcs - Grain size or dendrite cell size of experiment sample
# r0 - Initial radius of a spherical void
# volF - Initial void volume fraction
# period - Time period (0=no model)
# rate - Strain rate
# incr - No. of increments (0=no model)
# angle - Bi-axial loading ratio
# e_load - Strain level for load change (dstype 4 & 5)
#
material= hy100steel
G= 0
Bulk= 0
a= 0
b= 0
Tmelt= 3000
heat= 0.34
Kic= 1000
nv= 0.3
fname= T1R1P3.B1
source= DR. T. NICHOLAS; MATERIAL BEHAVIOR AT HIGH STRAIN RATES; WRIGHT-PATTERSON AFB, OHIO
comment= STRESS V. STRAIN; REF: BLESS, UDRI (1984)
excluded= 0
dstype= 1
units= 5
Tinit= 293
dn= 0
fn= 0.001
dcs0= 30
dcs= 30
r0= 0
volF= 0
period= 0.000269527
rate= 1100
incr= 100
angle= 0.51
e_load= 0
btype= 0

# Experimental data
strain, stress=
-0.00020373 0.75703
0.0003615 86.769
0.0010366 184.96
0.0017626 291.27
0.0020983 390.21
0.0024367 487.89
0.0029234 579.22
0.0035189 683.25
0.0042884 768.51
0.004795 850.2
0.0052728 913.13
0.005493 969.96
0.019381 985.08
0.033472 999.69
0.038596 1004.9
0.048385 1009.3
0.061821 1013.7
0.073908 1017.4
0.080058 1017
0.089921 1017.8
0.097754 1020.1
0.10452 1017.2
0.10972 1015.9
0.11763 1014.6
0.1273 1010.8
0.13609 1006.2
0.14793 998.97
0.15699 995.43
0.16952 982.1
0.17793 969.15
0.18897 953.49
0.2001 933.53
0.21136 911.78
0.22086 891.77
0.23397 858.92
0.24926 812.94
0.26272 773
0.27694 726.74
0.29648 655.52