# Data set for Damage Model v.1.0
#
model_tag= DMG

# Fields in the data set
# material - Tag for material
# G - Shear modulus
# Bulk - Bulk modulus
# a - Constant to adjust shear modulus due to variation of temperature from initial
# b - Constant to adjust bulk modulus due to variation of temperature from initial
# Tmelt - Melt temperature (K)
# heat - Heat generation term
# Kic - Particle fracture toughness
# nv - Particle McClintock damage constant
# fname - Tag for data set
# source - Source of data set
# comment - Any other comment on data set
# excluded - Is dataset excluded? 0=no, 1=yes
# dstype - Experiment type: 1=Tension 2=Compression 3=Torsion 4=Tens+Comp 5=Comp+Tens
# units - Stress units: 1=psi 2=Ksi 3=Pa  4=KPa 5=MPa 6=GPa
# Tinit - Initial temperature
# strain - strain values
# stress - stress values
# dn - Particle average size
# fn - Particles volume fraction
# dcs0 - Reference grain size or dendrite cell size
# dcs - Grain size or dendrite cell size of experiment sample
# r0 - Initial radius of a spherical void
# volF - Initial void volume fraction
# period - Time period (0=no model)
# rate - Strain rate
# incr - No. of increments (0=no model)
# angle - Bi-axial loading ratio
# e_load - Strain level for load change (dstype 4 & 5)
#
material= c1008steel
G= 0
Bulk= 0
a= 0
b= 0
Tmelt= 3000
heat= 0.34
Kic= 1000
nv= 0.3
fname= T1R1N3.A1
source= DR. T. NICHOLAS; MATERIAL BEHAVIOR AT HIGH STRAIN RATES; WRIGHT-PATTERSON AFB, OHIO
comment= STRESS V. STRAIN; REF: BLESS, UDRI (1984)
excluded= 0
dstype= 1
units= 5
Tinit= 293
dn= 0
fn= 0.001
dcs0= 30
dcs= 30
r0= 0
volF= 0
period= 226.94
rate= 0.001
incr= 100
angle= 0.51
e_load= 0
btype= 0

# Experimental data
strain, stress=
1.4603e-006 0.25055
0.00024787 58.012
0.00045629 112.49
2.7314e-005 162.81
0.00029945 215.51
0.00030984 260.13
-9.7349e-005 290.48
0.0037991 263.33
0.0074099 240.61
0.012275 224.43
0.017861 219.61
0.022894 217.96
0.027874 218.97
0.031563 217.61
0.035019 225.23
0.039466 238.38
0.046938 251.08
0.056785 265.24
0.067867 276.96
0.07925 285.64
0.091297 293.41
0.10577 299.99
0.12218 306.39
0.1362 310.32
0.15292 314.31
0.1725 318.09
0.19096 319.26
0.20756 320.72
0.22694 321.48