# Data set for Damage Model v.1.0
#
model_tag= DMG

# Fields in the data set
# material - Tag for material
# G - Shear modulus
# Bulk - Bulk modulus
# a - Constant to adjust shear modulus due to variation of temperature from initial
# b - Constant to adjust bulk modulus due to variation of temperature from initial
# Tmelt - Melt temperature (K)
# heat - Heat generation term
# Kic - Particle fracture toughness
# nv - Particle McClintock damage constant
# fname - Tag for data set
# source - Source of data set
# comment - Any other comment on data set
# excluded - Is dataset excluded? 0=no, 1=yes
# dstype - Experiment type: 1=Tension 2=Compression 3=Torsion 4=Tens+Comp 5=Comp+Tens
# units - Stress units: 1=psi 2=Ksi 3=Pa  4=KPa 5=MPa 6=GPa
# Tinit - Initial temperature
# strain - strain values
# stress - stress values
# dn - Particle average size
# fn - Particles volume fraction
# dcs0 - Reference grain size or dendrite cell size
# dcs - Grain size or dendrite cell size of experiment sample
# r0 - Initial radius of a spherical void
# volF - Initial void volume fraction
# period - Time period (0=no model)
# rate - Strain rate
# incr - No. of increments (0=no model)
# angle - Bi-axial loading ratio
# e_load - Strain level for load change (dstype 4 & 5)
#
material= s7toolsteel
G= 0
Bulk= 0
a= 0
b= 0
Tmelt= 3000
heat= 0.34
Kic= 1000
nv= 0.3
fname= S1R9P0.A1
source= HONEYWELL; G.R. JOHNSON AND T.J. HOLMQUIST; TEST DATA AND COMPUTATIONAL STRENGTH AND FRACTURE MODEL CONSTANTS FOR 23 MATERIALS SUBJECTED TO LARGE STRAINS, HIGH STRAIN RATES, AND HIGH TEMPERATURES; SEPTEMBER 1988
comment= SHEAR STRESS V. SHEAR STRAIN (converted to Von Mises)
excluded= 0
dstype= 3
units= 5
Tinit= 293
dn= 0
fn= 0.001
dcs0= 30
dcs= 30
r0= 0
volF= 0
period= 0.0590403
rate= 9.2
incr= 100
angle= 0.51
e_load= 0
btype= 0

# Experimental data
strain, stress=
0.000450599 1.85347
0.000875667 200.173
0.00130308 383.649
0.00187448 568.979
0.00460968 819.191
0.0073439 1061.97
0.00601945 1276.95
0.00783926 1414.17
0.0141612 1523.44
0.020933 1625.43
0.0394197 1729.07
0.0637568 1792.15
0.0880921 1814.15
0.132254 1823.5
0.172807 1814.15
0.223267 1788
0.254802 1758.38
0.298507 1739.67
0.347172 1728.48
0.416108 1732.05
0.479645 1737.42
0.500372 1748.51
0.517496 1752.32
0.543171 1707.7