# Data set for Damage Model v.1.0
#
model_tag= DMG

# Fields in the data set
# material - Tag for material
# G - Shear modulus
# Bulk - Bulk modulus
# a - Constant to adjust shear modulus due to variation of temperature from initial
# b - Constant to adjust bulk modulus due to variation of temperature from initial
# Tmelt - Melt temperature (K)
# heat - Heat generation term
# Kic - Particle fracture toughness
# nv - Particle McClintock damage constant
# fname - Tag for data set
# source - Source of data set
# comment - Any other comment on data set
# excluded - Is dataset excluded? 0=no, 1=yes
# dstype - Experiment type: 1=Tension 2=Compression 3=Torsion 4=Tens+Comp 5=Comp+Tens
# units - Stress units: 1=psi 2=Ksi 3=Pa  4=KPa 5=MPa 6=GPa
# Tinit - Initial temperature
# strain - strain values
# stress - stress values
# dn - Particle average size
# fn - Particles volume fraction
# dcs0 - Reference grain size or dendrite cell size
# dcs - Grain size or dendrite cell size of experiment sample
# r0 - Initial radius of a spherical void
# volF - Initial void volume fraction
# period - Time period (0=no model)
# rate - Strain rate
# incr - No. of increments (0=no model)
# angle - Bi-axial loading ratio
# e_load - Strain level for load change (dstype 4 & 5)
#
material= brass
G= 0
Bulk= 0
a= 0
b= 0
Tmelt= 3000
heat= 0.34
Kic= 1000
nv= 0.3
fname= T3R4P2.A1
source= HONEYWELL; G.R. JOHNSON AND T.J. HOLMQUIST; TEST DATA AND COMPUTATIONAL STRENGTH AND FRACTURE MODEL CONSTANTS FOR 23 MATERIALS SUBJECTED TO LARGE STRAINS, HIGH STRAIN RATES, AND HIGH TEMPERATURES; SEPTEMBER 1988
comment= TRUE STRESS V. TRUE STRAIN
excluded= 0
dstype= 1
units= 5
Tinit= 633
dn= 0
fn= 0.001
dcs0= 30
dcs= 30
r0= 0
volF= 0
period= 0.000486618
rate= 411
incr= 100
angle= 0.51
e_load= 0
btype= 0

# Experimental data
strain, stress=
6.2555e-005 0.17191
4.6566e-005 28.447
9.7886e-005 60.362
0.00028212 96.436
0.0069482 114.05
0.015756 131.85
0.026836 149.84
0.038304 161.6
0.046369 170.9
0.056961 177.97
0.070394 185.06
0.084836 192.53
0.097322 199.79
0.11031 207.58
0.12128 213.78
0.13396 220.7
0.1479 228.15
0.16341 235.63
0.17924 242.07
0.19186 248.11
0.2 250.99